Aquivion(R) P87S-SO2F cylindrical pellets 2mm, PFSF eq. wt. (870 g/mole SO2F), contains CF3 polymer chain ends as stabilizer

Uses

• Aquivion^? P87S pellets can be melt-pressed or extruded into plates, sheets or thin films down to about 50μ. The extruder shall be equipped with a standard three-zone metering screw devoid of barrier or mixing elements. Optimum temperature settings will depend on the configuration of the equipment but generally cover 100 to 300°C range. Optionally functional groups in the molded part are then hydrolyzed in baths or wet benches with a heated base (NaOH, KOH etc), reaction which may take minutes or hours, depending on thickness and conditions.
• Aquivion^? P87S pellets can be directly hydrolyzed as described - either completely or only on their outer surface. This will enable functional activity of the sulfonic acid / sulfonyl salt groups for ion-exchange operations or as acid catalyst.

Uses

Aquivion^? P98 pellets can be melt-pressed or extruded into plates, sheets or thin films down to about 50μ. The extruder shall be equipped with a standard three-zone metering screw devoid of barrier or mixing elements. Optimum temperature settings will depend on the configuration of the equipment but generally cover 100 to 300°C range. Optionally functional groups in the molded part are then hydrolyzed in baths or wet benches with a heated base (NaOH, KOH etc), reaction which may take minutes or hours, depending on thickness and conditions.
Aquivion^? P98 pellets can be directly hydrolyzed as described - either completely or only on their outer surface. This will enable functional activity of the sulfonic acid /sulfonyl salt groups for ion-exchange operations or as acid catalyst.

General Description

Aquivion^? P87S-SO₂F are pellets based on the short-side-chain (SSC) copolymer of Tetrafluoroethylene and the Sulfonyl Fluoride Vinyl Ether (SFVE) CF₂=CF₂-O-(CF₂)₂-SO₂F industrially produced by Solvay Specialty Polymers. The resulting perfluoropolymer′s functional groups are in their sulfonyl fluoride form, SO₂F. The polymer of this grade is chemically stabilized and therefore contains a maximized ratio of inert R-CF₃ end-groups.