ポリ(ビニルメチルエーテル) (50%メタノール溶液)
ポリ(ビニルメチルエーテル) (50%メタノール溶液) 物理性質
- 融点 :
- 112-144 °C
- 比重(密度) :
- 1.03 g/mL at 25 °C
- 蒸気圧:
- 0.03 atm ( 20 °C)
- 屈折率 :
- n20/D 1.467
- 水溶解度 :
- Soluble in water
- 外見 :
- clear liquid
- 色:
- Colorless to Yellow to Orange
- SMILES:
- C(OC)(CC(*)OC)CC(OC)C* |$;;;;;*;;;;;;;;*$|
- CAS データベース:
- 9003-09-2
- EPAの化学物質情報:
- Ethene, methoxy-, homopolymer (9003-09-2)
安全性情報
- リスクと安全性に関する声明
- 危険有害性情報のコード(GHS)
| Rフレーズ |
36/37/38 |
|
|
| Sフレーズ |
26-36/37/39 |
|
|
| RIDADR |
UN 1230 3/6.1/PG II |
|
|
| WGK Germany |
1 |
|
|
| HSコード |
2909.19.6000 |
|
|
| 国連危険物分類 |
3/6.1 |
|
|
| 容器等級 |
II |
|
|
| 消防法 |
危-4-1-II |
|
|
| 化審法 |
(6)-982 |
|
|
| 安衛法 |
有機則 第二種有機溶剤等 |
|
|
| 絵表示（GHS） |
  
|
| 注意喚起語 |
危険 |
| 危険有害性情報 |
| コード |
危険有害性情報 |
危険有害性クラス |
区分 |
注意喚起語 |
シンボル |
P コード |
| H225 |
引火性の高い液体および蒸気 |
引火性液体 |
2 |
危険 |
|
P210,P233, P240, P241, P242, P243,P280, P303+ P361+P353, P370+P378,P403+P235, P501 |
| H319 |
強い眼刺激 |
眼に対する重篤な損傷性/眼刺激 性 |
2A |
警告 |
|
P264, P280, P305+P351+P338,P337+P313P |
| H335 |
呼吸器への刺激のおそれ |
特定標的臓器毒性、単回暴露； 気道刺激性 |
3 |
警告 |
|
|
| H336 |
眠気やめまいのおそれ |
特定標的臓器毒性、単回暴露； 麻酔作用 |
3 |
警告 |
|
P261, P271, P304+P340, P312,P403+P233, P405, P501 |
| H360 |
生殖能または胎児への悪影響のおそれ |
生殖毒性 |
1A, 1B |
危険 |
|
|
| H370 |
臓器の障害 |
特定標的臓器有害性、単回暴露 |
1 |
危険 |
|
P260, P264, P270, P307+P311, P321,P405, P501 |
| H372 |
長期にわたる、または反復暴露により臓器の障 害 |
特定標的臓器有害性、単回暴露 |
1 |
危険 |
|
P260, P264, P270, P314, P501 |
|
| 注意書き |
| P201 |
使用前に取扱説明書を入手すること。 |
| P202 |
全ての安全注意を読み理解するまで取り扱わないこ と。 |
| P210 |
熱/火花/裸火/高温のもののような着火源から遠ざ けること。－禁煙。 |
| P233 |
容器を密閉しておくこと。 |
| P240 |
容器を接地すること/アースをとること。 |
| P241 |
防爆型の電気機器/換気装置/照明機器/．．．機器を使 用すること。 |
| P242 |
火花を発生させない工具を使用すること。 |
| P243 |
静電気放電に対する予防措置を講ずること。 |
| P260 |
粉じん/煙/ガス/ミスト/蒸気/スプレーを吸入しないこ と。 |
| P264 |
取扱い後は皮膚をよく洗うこと。 |
| P264 |
取扱い後は手や顔をよく洗うこと。 |
| P270 |
この製品を使用する時に、飲食または喫煙をしないこ と。 |
| P271 |
屋外または換気の良い場所でのみ使用すること。 |
|
ポリ(ビニルメチルエーテル) (50%メタノール溶液) 価格
もっと(7)
| メーカー |
製品番号 |
製品説明 |
CAS番号 |
包装 |
価格 |
更新時間 |
購入 |
|
富士フイルム和光純薬株式会社(wako)
|
W01POS03032 |
ポリビニルメチルエーテル、50%水溶液
Poly(vinyl methyl ether), 50% soln. in water |
9003-09-2 |
500g |
￥73500 |
2024-03-01 |
購入 |
|
東京化成工業
|
P0384 |
ポリ(メチルビニルエーテル) (30%水溶液)
Poly(methyl Vinyl Ether) (30% in Water)
|
9003-09-2 |
25g |
￥2500 |
2024-03-01 |
購入 |
|
東京化成工業
|
P0384 |
ポリ(メチルビニルエーテル) (30%水溶液)
Poly(methyl Vinyl Ether) (30% in Water)
|
9003-09-2 |
500g |
￥7700 |
2024-03-01 |
購入 |
|
Sigma-Aldrich Japan
|
182729 |
ポリ(メチルビニルエーテル) 溶液 50?wt. % in H2O
Poly(methyl vinyl ether) solution 50?wt. % in H2O |
9003-09-2 |
500g |
￥42300 |
2024-03-01 |
購入 |
|
Sigma-Aldrich Japan
|
182729 |
ポリ(メチルビニルエーテル) 溶液 50?wt. % in H2O
Poly(methyl vinyl ether) solution 50?wt. % in H2O |
9003-09-2 |
25g |
￥6230 |
2023-06-01 |
購入 |
ポリ(ビニルメチルエーテル) (50%メタノール溶液) 化学特性,用途語,生産方法
外観
うすい黄色～褐色透明液体～わずかに濁った液体
外観
無色～黄色～黄赤色透明液体
定義
ChEBI: A macromolecule composed of repeating methoxyethyl groups.
製造方法
Vinyl ethers are prepared by reaction of acetylene and alcohols in the
presence of the potassium alkoxide as catalyst:
For the production of polymers, methyl, ethyl and isobutyl vinyl ethers are
the most common monomers.
Vinyl ethers are susceptible only to cationic polymerization. In a typical process, methyl vinyl ether is agitated with boron
trifluoride (BF 3. 2H20). The temperature is kept at about l0?? by cooling
for 3-4 hours; the reactor is then sealed and the temperature allowed to rise
to 100??C. Reaction is complete in about 10 hours and the polymer is obtained
as a viscous mass. It is interesting to note that poly(vinyl isobuty ether) may
be obtained in crystalline form by conducting polymerization at - 80?? to
-60??C in liquid propane using boron trifluoride etherate as initiator. This
was the first stereoregular polymerization to be achieved. Incidentally,
isotactic polymer has also been prepared by the use of Ziegler-Natta type
catalysts and this was the first indication that these catalysts could polymerize a suitable monomer by a cationic mechanism.
Poly(vinyl methyl ether) is water-soluble and is used in adhesive and textile sizes. The ethyl and isobutyl polymers find use in pressure-sensitive adhesives.
ポリ(ビニルメチルエーテル) (50%メタノール溶液) 上流と下流の製品情報
原材料
準備製品
ポリ(ビニルメチルエーテル) (50%メタノール溶液) 生産企業
Global( 81)Suppliers
ポリ(ビニルメチルエーテル) (50%メタノール溶液) スペクトルデータ(IR1)
9003-09-2(ポリ(ビニルメチルエーテル) (50%メタノール溶液))キーワード:
- 9003-09-2
- VINYL METHYL ETHER POLYMER
- Ethene,methoxy-,homopolymer
- methoxy-ethenhomopolymer
- poly(vinylmethylether)(70%intoluene)
- Ether, methyl vinyl, polymers
- Gantre m-154
- Gantrez m
- Gantrez m 093
- Gantrez m 094
- Gantrez m 154
- Poly(vinyl Methyl Ether) (50% in Methanol)
- vinyl methyl ether homopolymer
- Poly(methyl Vinyl Ether) (30% in Water)
- poly(vinyl ether)
- Poly(vinyl Methyl Ether) (30% in Water)
- Poly(methyl vinyl ether) solution
- Poly(vinyl methyl ether) (50% in toluene)
- POLY(METHYL VINYL ETHER), 50 WT. % SOLUT ION IN WATER
- Polyvinylmethylether, mittlere Molmasse 52000 g/mol
- POLY(VINYL METHYL ETHER): (50% IN WATER)
- POLY(METHYL VINYL ETHER)
- METHYL VINYL ETHER POLYMER
- Gantrez m 574
- Gantrez m-094
- Poly(Methyl vinyl ether) solution 50 wt. % in H2O
- Methyl Vinyl Ether Polymer
Poly(methyl Vinyl Ether)
Vinyl Methyl Ether Polymer
- Methyl Vinyl Ether Polymer
Poly(vinyl Methyl Ether)
Vinyl Methyl Ether Polymer
- poly(vinyl methyl ether) macromolecule
- POLY(VINYL METHYL ETHER)
- Poly(vinyl methyl ether)， Approx Mw: 90,000 [GPC]
- ポリ(ビニルメチルエーテル) (50%メタノール溶液)
- ポリ(メチルビニルエーテル) （30%水溶液)
- ポリビニルエ-テル
- ポリビニルエーテル
- ビニルメチルエーテルポリマー (30%水溶液)
- ビニルメチルエーテルポリマー (50%メタノール溶液)
- ポリ(ビニルメチルエーテル) (30%水溶液)
- ポリ(メチルビニルエーテル) (50%メタノール溶液)
- メチルビニルエーテルポリマー (30%水溶液)
- メチルビニルエーテルポリマー (50%メタノール溶液)
- ポリビニルメチルエーテル、50%水溶液
- ポリ(メチルビニルエーテル) 溶液
- ポリ(ビニルメチルエーテル)